In order to overcome the shortcomings of conventional hot pressing, a novel near net-shape technique, called radial hot pressing, for P/M parts with large height-to-diameter (H/D) ratio was introduced. Effects of processing parameters on the microstructures and density of P/M TiAl base alloy valves were studied. Results show that the radial hot pressing is an effective technique for manufacturing valves with a H/D ratio of about 10:1, and the perfect joint interface between the Mo sheet and the parts is helpful for subsequent HIPing.
关键词:
Near net-shape technique
,
null
,
null
Hanwei HE
,
Kechao ZHOU
材料科学技术（英）
A new method for preparation of TaC coating on C/C composite material is reported. The amorphous ethylate tantalum jellied as the precursor is prepared and spread densely on the surface of the C/C composite material so as to form a multilayer film. In a graphitization furnace the multilayer film is transformed into TaC coating at various temperatures. Ethylate tantalum film is characterized by FT-IR (Fourier transform infrared) spectra, XRD (X-ray diffraction) and SEM (scanning electron microscopy) and TaC coating is characterized by XRD and SEM. At 1200℃ the coating contained TaC and Ta¬2O5, and at above 1400℃ only TaC is formed. The coating formed at 1600℃ is a continuous stratum structure, and that formed at 1600℃ is a porous net structure. Analysis on thermodynamics and formation mechanism of TaC indicates that, after ethylate tantalum is decomposed, Ta2O¬5 is first produced and then transformed into Ta2C, and newly formed Ta2C is transformed into TaC by the sufficient C at last.
关键词:
C/C composite
,
composite
,
material
,
TaC
,
coating
,
ethyl